Weight loss, electrochemical impedance and potentiodynamic polarization studies were done with the Mild steel in 0.5 M hydrochloric acid with the different concentration of pheniramine maleate (PM). The potentiodynamic polarization results showed as the concentration of pheniramine maleate increases the Icorr decreases and inhibition efficiency of Mild steel increases. From the result the good inhibition efficiency of pheniramine maleate is observed. The Surface analysis of mild steel in 0.5 M hydrochloric acid in the presence of pheniramine maleate was carried out by SEM and adsorption isotherm. The theoretical results obtained from DFT calculations were correlated with the experimental results.

Mild steel, 0.5 M hydrochloric acid, Pheniramine Maleate, Potentiodynamic polarization, Electrochemical impedance spectroscopy

"Anticorrosion Activity of Pheniramine Maleate on Mild Steel in Hydrochloric acid.", International Journal of Emerging Technologies and Innovative Research (www.jetir.org), ISSN:2349-5162, Vol.5, Issue 12, page no.432-438, December-2018, Available :http://www.jetir.org/papers/JETIR1812755.pdf

"Anticorrosion Activity of Pheniramine Maleate on Mild Steel in Hydrochloric acid.", International Journal of Emerging Technologies and Innovative Research (www.jetir.org | UGC and issn Approved), ISSN:2349-5162, Vol.5, Issue 12, page no. pp432-438, December-2018, Available at : http://www.jetir.org/papers/JETIR1812755.pdf