• K.S.Sonawane
• N.A.Davkhar
• J.A.Borse
• J.M.Shewale
• A.V.Patil

ZnS thin films deposited by two electrode electrochemical deposition using the two electrode system on stainless steel substrates from aqueous solution containing 0.3 N Zinc sulphate (ZnSO4·2H2O) and 0.2 N sodium thiosulphate (Na2S2O3). The 2 % Triethanolamine was used as a complex agent for complex form of ZnS materials. The Thickness of ZnS thin film was increases up to certain time after that it was found fall by co- deposition with deposition time. The voltage for deposition corresponding current density was optimized by polarization curve method. The good quality adherent films of ZnS were obtained at 1700 mv in two electrode system. The thickness of film was measured by mass difference method. The chemical bonding of functional group of deposited material was studied by IR spectral analysis.The Chemical Composition of ZnS analysed by EDAX.The Structural characterization and surface morphology was studied by XRD, SEM respectively.

ZnS, Electrochemical Deposition, IR, EDAX, SEM

"Physical Properties of Zinc Sulphide (ZnS) thin film by Electrochemical Deposition", International Journal of Emerging Technologies and Innovative Research (www.jetir.org), ISSN:2349-5162, Vol.6, Issue 4, page no.30-33, April-2019, Available :http://www.jetir.org/papers/JETIR1904606.pdf

"Physical Properties of Zinc Sulphide (ZnS) thin film by Electrochemical Deposition", International Journal of Emerging Technologies and Innovative Research (www.jetir.org | UGC and issn Approved), ISSN:2349-5162, Vol.6, Issue 4, page no. pp30-33, April-2019, Available at : http://www.jetir.org/papers/JETIR1904606.pdf