In the present research work, the single crystals of strontium doped barium tartrate (SrBaC4H4O6) crystals were grown by single diffusion technique. The optimum growth conditions for (SrBaC4H4O6) crystals were optimized by varying various parameters such as pH of the gel solution, gel concentration, gel setting time, concentration of the reactance. The platy shaped crystals were obtained in silica gel at room temperature. The effect of Strontium (Sr) doping on the barium tartrate (BaC4H4O6) has been studied. The XRD pattern shows that (SrBaC4H4O6) crystals are polycrystalline, having orthorhombic structure. The SEM pictures reveal that these crystals are grown by layer deposition. Thermo Gravimetric Analysis (TGA) curves show the percentages of the weight loss in the different stages of decomposition of barium tartrate. Differential Scanning Calorimetry (DSC) curves show the phase transformation due to loss of water molecules and formation of stable anhydrous (SrBaC4H4O6) crystals.

Sol gel technique, Strontium, Barium, XRD, SEM, TGA, DSC.

"Comparative Study of Thermal Stability of Strontium Doped Barium Tartrate Crystals by Silica Gel Technique ", International Journal of Emerging Technologies and Innovative Research (www.jetir.org), ISSN:2349-5162, Vol.6, Issue 3, page no.462-468, March-2019, Available :http://www.jetir.org/papers/JETIRAO06069.pdf

"Comparative Study of Thermal Stability of Strontium Doped Barium Tartrate Crystals by Silica Gel Technique ", International Journal of Emerging Technologies and Innovative Research (www.jetir.org | UGC and issn Approved), ISSN:2349-5162, Vol.6, Issue 3, page no. pp462-468, March-2019, Available at : http://www.jetir.org/papers/JETIRAO06069.pdf